Sains Malaysiana 43(1)(2014): 111–116

 

Effect of High-speed Parameters on Uncoated Carbide Tool in

Finish Turning Titanium Ti-6Al-4V ELI

(Kesan Parameter Berkelajuan Tinggi terhadap Mata Alat Berkabida tak Bersalut bagi Larikan Titanium Ti-6Al-4V ELI)

 

M.A. SULAIMAN2, C.H. CHE HARON1*, J.A. GHANI1& M.S. KASIM2

1Department of Mechanical and Material EngineeringFaculty of Engineering and Built Environment

Universiti Kebangsaan Malaysia, 43600 UKM Bangi, Selangor Darul Ehsan, Malaysia

 

2Department of Process, Faculty of Manufacturing Engineering, Universiti Teknikal Malaysia Melaka

76100 Hang Tuah Jaya, Melaka

 

Received: 21 March 2012/Accepted: 15 May 2012

 

ABSTRACT

In this work, the Sandvik uncoated carbide insert, CNGG 120408-SGF-H13A was used as a cutting tool in high-speed turning of titanium alloy Ti-6Al-4V ELI (extra-low interstitial) with hardness of 32 HRC. Wear is one of the problems that cannot be avoided in machining process. Therefore, the objective of this paper was to investigate tool-wear behavior of various cutting-speed values (high-speed range) on the tool life of the cutting tools, especially in finishing titanium alloy. The experiments were performed under flooded coolant condition using water-based mineral-oil. The cutting speeds employed were 120, 170 and 220 m/min. The feed rate was constant at 0.2 mm/rev and the depth of cut was 0.4 mm. Based on the results, the highest cutting speed of 220 m/min caused the highest wear rate. By linking the machine operations and the tool life curves obtained using flank wear data, the wear behavior of uncoated carbide was described.

 

Keywords: Coolant; high speed turning; Ti-6Al-4V ELI; uncoated carbide

 

ABSTRAK

Dalam kajian ini, mata pemotong karbida tidak bersalut buatan Sandvik; CNGG 120408-SGF-H13A telah digunakan sebagai alat pemotongan dalam larikan kelajuan tinggi terhadap titanium aloi Ti-6Al-4V ELI (tambahan rendah celahan) yang mempunyai kekerasan 32 HRC. Kehausan mata pemotong adalah salah satu masalah yang tidak dapat dielakkan dalam proses melarik. Oleh itu, objektif kajian ini adalah untuk melihat kelakuan kehausan mata pemotong pada pelbagai nilai kelajuan pemotongan (pada julat kelajuan tinggi) terhadap jangka hayat mata pemotong terutama untuk proses larikan akhiran titanium aloi. Eksperimen ini telah dilakukan di bawah keadaan penyejuk banjir dengan menggunakan minyak mineral berasaskan air. Kelajuan pemotongan adalah 120, 170 dan 220 m/min. Sementara itu, kadar suapan adalah malar pada kadar 0.2 mm/pusingan dan kedalaman pemotongan pada 0.4 mm. Berdasarkan keputusan yang diperoleh, didapati bahawa kelajuan pemotongan tertinggi, 220 m/min mengakibatkan kadar kehausan yang tertinggi pada mata pemotong. Dengan menghubungkan operasi pemesinan dan keluk hayat mata pemotong yang diperoleh dengan menggunakan data haus rusuk, kelakuan haus karbida tidak bersalut telah diterangkan.

 

Kata kunci: Karbida tidak bersadur; larikan berkelajuan tinggi; pelinciran; Ti-6Al-4V ELI

REFERENCES

 

Boyer, R.R. 1995. Titanium for aerospace: Rationale and application. Advanced Performance Material 2(4): 349-368.

Che Haron, C.H. 2001. Tool life and surface integrity in turning titanium alloy. Journal of Material Processing and Technology 118: 231-237.

Che Haron, C.H., Ginting, A. & Goh, J.H. 2001. Wear of coated and uncoated carbides in turning tool steel. Journal of Materials Processing and Technology 116: 49-54.

Che Hassan, C.H. & Jawaid, A. 2005. The effect of machining on surface integrity of titanium alloy Ti-6%Al-4%V. Journal of Materials Processing and Technology 166: 188-192.

Dernley, P.A. & Grearson, A.N. 1986. Evaluation of principal wear mechanisms of cemented carbides and ceramics used for machining titanium alloy IMI 318. Material Science and Technology 2(1): 47-58.

Ezugwu, E.O. & Wang, Z.M. 1997. Titanium alloys and their machinability – A review. Journal of Materials Processing and Technology 68: 262-274.

Ezugwu, E.O. 2005. Key improvement in the machining of difficult-to-cut aerospace super alloys. International Journal of Machine Tools and Manufacture 45: 1353-1367.

Ezugwu, E.O., Da Silva, R.B., Bonney, J. & Machado, A.R. 2005. Evaluation of the performance of CBN tools when turning Ti-6Al-4V alloy with high pressure coolant supplies. International Journal Machine Tools and Manufacture 45: 1009-1014.

Ezugwu, E.O., Booney, J. & Yamane, Y. 2003. An overview of the machinability of aeroengine alloys. Journal of Material Processing and Technology 134: 233-253.

Gusri, A.I., Che Hassan, C.H. & Jaharah, A.G. 2008. The effect of dry machining on surface integrity of titanium alloy Ti- 6Al-4V ELI. Journal of Applied Science 1: 121-127.

Ginting, A. 2003. Pemesinan hijau aloi titanium Ti-6242S dengan menggunakan perkakas pemotong pengisar hujung karbida. Tesis Dr. Falsafah, Jabatan Kejuruteraan Mekanik dan Bahan. Universiti Kebangsaan Malaysia (unpublished).

Groover, M.P. 2007. Fundamentals of Modern Manufacturing. 3rd ed. United States: John Wiley & Sons.

ISO 3685. 1977. Tool Life Testing with Single-point Turning Tools. Geneva: International Standard Organization.

Jawaid, A., Che Haron, C.H. & Abdullah, A. 1999. Tool wear characteristics in turning of titanium alloy Ti-6246. Journal Material Processing and Technology 92: 329-334.

Jawaid, A., Sharif, S. & Koksal, S. 2000. Evaluation of wear mechanism of coated carbide tools when face milling titanium alloy. Journal of Materials Processing and Technology 99(1- 3): 266-274.

Machado, A.R. & Wallbank, J. 1990. Machining of titanium and its alloys - A review. Journal of Engineering Manufacture 204: 53-60.

Nabhani, F. 2001. Machining of aerospace titanium alloys. Robotics and Computer Integrated Manufacturing 17: 99- 106.

Narutaki, N. & Yamane, Y. 1993. Machining of difficult-to-cut material. International Journal Japan Soc. Prec. Engineering 27(4): 307-310.

Ribeiro, M.V., Moreira, M.R.V. & Ferreira, J.R. 2003. Optimization of titanium alloy (Ti-6Al-4V) machining. Journals of Materials Processing and Technology 143-144: 458-463.

Venkatesh, V.C. 1980. Tool wears investigations on some cutting tool materials. Journal Lubrication Technology 102: 556-559.

 

 

*Corresponding author; email: chase@eng.ukm.my

 

 

 

previous