Sains Malaysiana 43(9)(2014): 1373–1378

 

Characterization of Cerate-Zirconate Ceramics Powder Prepared by

Three Different Methods: A Comparative Study

(Pencirian Serat-Zirkonat Seramik Serbuk Disediakan oleh Tiga Kaedah yang Berbeza:

Suatu Kajian Perbandingan)

 

 

NAFISAH OSMAN1*, NAJWA ‘ADNI IBARAHIM1,2, MOHD AZLAN MOHD ISHAK1 & OSKAR HASDINOR HASSAN3

 

1Faculty of Applied Sciences, Universiti Teknologi MARA, 02600 Arau, Perlis

Malaysia

 

2Faculty of Applied Sciences, Universiti Teknologi MARA, 40450 Shah Alam,

Selangor Darul Ehsan, Malaysia

 

3Faculty of Art and Design, Universiti Teknologi MARA, 40450 Shah Alam,

Selangor Darul Ehsan, Malaysia

 

Received: 15 May 2013/Accepted: 1 May 2014

 

ABSTRACT

Ceramics powder of BaCe0.54Zr0.36Y0.1O2.95 (BCZY) was synthesized using three different methods namely sol-gel (SG), supercritical fluid (SC) and supercritical fluid assisted sol-gel (SCSG). The respective prepared samples were denoted as S1, S2 and S3. TG thermogram of the dried powders for all samples showed three stages of weight loss. Each stage was corroborated by one or two exothermic peaks as shown in DTG signal. Complete thermal decomposition for all the samples was almost accomplished at 1000°C for about 2 h. At calcination temperature of 1100°C, S1 showed a single-phase of perovskite-type oxides as proven by XRD result. Morphology of the calcined powders by SEM micrograph showed that S1 is in spherical shape, S2 is in cubic structure and S3 has a mixture of spherical and rod-like structure. Therefore, as comparison, SG method gives better characteristics of cerate-zirconate ceramics powder compared to SC and SGSC.

 

Keywords: Cerate-zirconate ceramic; sol-gel; supercritical fluid; supercritical fluid assisted sol-gel

 

ABSTRAK

Serbuk seramik BaCe0.54Zr0.36Y0.1O2.95 (BCZY) telah disintesis menggunakan tiga kaedah yang berbeza iaitu sol-gel (SG), bendalir lampau genting (SC) dan bendalir lampau genting dibantu sol-gel (SGSC). Sampel masing-masing telah ditandakan sebagai S1, S2 dan S3. Isyarat TG bagi semua serbuk sampel yang dikeringkan telah menunjukkan tiga peringkat kehilangan berat. Setiap peringkat kehilangan diiringi oleh satu atau dua puncak eksotermik seperti ditunjukkan oleh isyarat DTG. Penguraian terma yang lengkap untuk semua sampel didapati hampir sempurna pada suhu 1000°C selama 2 jam. Pada suhu pengkalsinan 1100°C, S1 menunjukkan satu fasa tunggal oksida perovksite seperti dibuktikan oleh analisis XRD. Morfologi serbuk yang dikalsinkan menggunakan mikrograf SEM mendedahkan S1 adalah dalam bentuk sfera, S2 berbentuk kubus dan S3 adalah campuran bentuk sfera dan rod. Sebagai perbandingan, didapati kaedah SG memberi ciri serbuk seramik serat-zirkonat yang lebih baik daripada SC dan SGSC.

 

Kata kunci: Cecair genting lampau; cecair genting lampau membantu sol-gel; serat-zirkonat seramik; sol-gel

 

REFERENCES

Abdullah, N.A., Osman, N., Hasan, S. & Hassan, O.S. 2012. Chelating agents role on thermal characteristics and phase formation of modified cerate-zirconate via sol-gel synthesis route. International Journal of Electrochemical Sciences 7: 9401-9404.

Aymonier, C., Loppinet-Serani, A., Reverón, H., Garrabos, Y. & Cansell, F. 2006. Review of supercritical fluids in organic material science. Journal of Supercritical Fluids 38: 242-251.

Bozbag, S.E. & Erkey, C. 2012. Supercritical fluids in fuel cell research and development. The Journal of Supercritical Fluids 62: 1-31.

Byrappa, K., Ohara, S. & Adschiri, T. 2008. Nanoparticles synthesis using supercritical fluid technology - towards biomedical applications. Advanced Drug Delivery Reviews 60(3): 299-327.

Caba˜nas, A., Li, J., Blood, P., Chudoba, T., Lojkowski, W., Poliakoff, M. & Lester, E. 2007. Synthesis of nanoparticulate yttrium aluminum garnet in supercritical water-ethanol mixtures. Journal of Supercritical Fluids 40: 284-292.

Chakroborty, A., Sharma, A.D., Maiti, B. & Maiti, H.S. 2002. Preparation of low-temperature sinterable BaCe0.8Sm0.2O3 powder by autoignition technique. Materials Letters 57: 862-867.

Fabbri, E., D’Epifanio, A., Di Bartolomeo, E., Licoccia, S. & Traversa, E. 2008. Tailoring the chemical stability of Ba(Ce0.8-xZrx)Y0.2O3-δ protonic conductors for Intermediate Temperature Solid Oxide Fuel Cells (IT-SOFCs). Solid State Ionics 179(15-16): 558-564.

Ishak, M.A.M. 2007. A study on liquefaction of pretreted Mukah Balingan low rank Malaysia coal. PhD Thesis. Universiti Teknologi MARA (Unpublished). pp. 99-123.

Kim, J., Kim, D., Veriansyah, B., Kang, J.W. & Kim, J.D. 2009. Metal nanoparticle synthesis using supercritical alcohol. Materials Letters 63(21): 1880-1882.

Lazarević, Z.Ž., Vijatović, M., Dohčević-Mitrović, Z., Romčević, N.Ž., Romčević, M.J., Paunović, N. & Stojanović, B.D. 2010. The characterization of the barium titanate ceramic powders prepared by the Pechini type reaction route and mechanically assisted synthesis. Journal of the European Ceramic Society 30(2): 623-628.

Nityanand, C., Nalin, W.B., Rajkumar, B.S. & Chandra, C.M. 2011. Synthesis and physicochemical characterization of nanocrystalline cobalt doped lanthanum strontium ferrite. Solid State Sciences 13(5): 1022-1030.

Osman, N., Jani, A.M. & Talib, I.A. 2006. Synthesis of Yb-doped Ba(Ce,Zr)O3 ceramic powders by sol-gel method. Ionics 12: 379-384.

Patra, H., Rout, S.K., Pratihar, S.K. & Bhattacharya, S. 2011. Effect of process parameters on combined EDTA-citrate synthesis of Ba0.5Sr0.5Co0.8Fe0.2O3-δ perovskite. Powder Technology 209: 98-104.

Piticescu, R.M., Vilarnho, P., Popescu, L.M. & Piticescu, R.R. 2006. Perovskite nanostructures obtained by a hydrothermal electrochemical process. Journal of the European Ceramic Society 26(14): 2945-2949.

Ru, Y., Jie, Q., Min, L. & Guoqiang, L. 2008. Synthesis of yttrium aluminum garnet (YAG) powder by homogeneous precipitation combined with supercritical carbon dioxide or ethanol fluid drying. Journal of the European Ceramic Society 28: 2903-2914.

Ryu, K.H. & Haile, S.M. 1999. Chemical stability and proton conductivity of doped BaCeO3 –BaZrO3 solid solutions. Solid State Ionics 125: 355-367.

Singh, K.A., Pathak, L.C. & Roy, S.K. 2007. Effect of citric acid on the synthesis of nano-crystalline yttria stabilized zirconia powders by nitrate–citrate process. Ceramics International 33(8): 1463-1468.

Singh, R.C., Singh, M.P., Singh, O. & Chandi, P.S. 2009. Influence of synthesis and calcination temperatures on particle size and ethanol sensing behaviour of chemically synthesized SnO2 nanostructures. Sensors and Actuators B 143: 226-232.

Wang, S., Zhao, F., Zhang, L. & Chen, F. 2011. Synthesis of BaCe0.7Zr0.1Y0.1Yb0.1O3-δ proton conducting ceramic by a modified Pechini method. Solid State Ionics 213: 29-35.

Zhong, Z. 2007. Stability and conductivity study of the BaCe0.9-xZrxY0.1O2.95 systems. Solid State Ionics 178: 213-220.

 

*Corresponding author; email; fisha@perlis.uitm.edu.my

 

 

previous