Sains Malaysiana 44(4)(2015): 607–612

 

Decolorization and Mineralization of Batik Wastewater through Solar Photocatalytic Process

(Penyahwarnaan dan Penguraian Sisa Air Batik melalui Proses Fotopemangkinan Cahaya Matahari)

 

 

WAN FADHILAH KHALIK1, LI-NGEE HO*2, SOON-AN ONG1, YEE-SHIAN WONG1,

NIK ATHIRAH YUSOFF1 & FAHMI RIDWAN1

 

1Water Research Group, School of Environmental Engineering,Universiti Malaysia Perlis, 02600 Arau, Perlis, Malaysia

 

2School of Material Engineering, Universiti Malaysia Perlis, 02600 Arau, Perlis, Malaysia

 

Received: 26 September 2014/Accepted: 3 December 2014

 

ABSTRACT

In this study, the photocatalytic degradation of batik wastewater in the presence of zinc oxide (ZnO) as photocatalyst was investigated. The effect of various operating parameters, such as pH of batik wastewater, catalyst dosage and aeration on the photocatalytic degradation process, was examined. The mineralization of batik wastewater was also evaluated through chemical oxygen demand analysis. The decolorization of batik wastewater was enhanced at acidic conditions (pH3) which was 88.2% after 10 h irradiated under solar light, meanwhile its mineralization was 286 mg/L after 12 h irradiation time. The data obtained for photocatalytic degradation of batik wastewater was well fitted with the Langmuir-Hinshelwood kinetic model. It can be concluded that batik wastewater could be decolorized and mineralized under solar light irradiation with presence of ZnO.

 

Keywords: Batik wastewater; decolorization; mineralization; photocatalytic; zinc oxide

 

ABSTRAK

Di dalam kertas ini, degradasi sisa air batik oleh fotopemangkinan dengan kehadiran zink oksida sebagai fotopemangkin telah dikaji. Kesan daripada pelbagai parameter operasi, contohnya, pH sisa air batik, dos fotopemangkin dan pengudaraan ke atas proses fotopemangkinan telah dikaji. Penguraian sisa air batik juga dinilai melalui analisis permintaan oksigen kimia. Penyahwarnaan sisa air batik meningkat dalam keadaan berasid (pH3) iaitu 88.2% selepas 10 jam diradiasi di bawah cahaya matahari, sementara itu, penguraiannya ialah 286 mg/L selepas 12 jam masa penyinaran. Data yang diperoleh untuk degradasi fotopemangkinan sisa air batik adalah mengikut model kinetik Langmuir-Hinshelwood. Dapat disimpulkan bahawa sisa air batik boleh dinyahwarnakan dan diuraikan di bawah penyinaran cahaya matahari dengan kehadiran zink oksida.

 

Kata kunci: Fotopemangkinan; penguraian; penyahwarnaan; sisa air batik; zink oksida

REFERENCES

Akyol, A. & Bayramoğlu, M. 2005. Photocatalytic degradation of Remazol Red F3B using ZnO catalyst. Journal of Hazardous Materials B124: 241-246.

Akyol, A., Yatmaz, H.C. & Bayramoğlu, M. 2004. Photocatalytic decolorization of Remazol Red RR in aqueous ZnO suspensions. Applied Catalysis B: Environmental 54: 19-24.

Arslan, I. & Balcioglou, I.A. 1999. Degradation of commercial reactive dyestuffs by heterogeneous and homogenous advanced oxidation processes: A comparative study. Dyes Pigments 43: 95-108.

Badawy, M.I., Gohary, F.E., Ghaly, M.Y. & Ali, M.E.M. 2009. Enhancement of olive mill wastewater biodegradation by homogeneous and heterogeneous photocatalytic oxidation. Journal of Hazardous Materials 169: 673-679.

Behnajady, M.A., Modirshahla, N. & Hamzavi, R. 2006. Kinetic study on photocatalytic degradation of C.I. Acid Yellow 23 by ZnO photocatalyst. Journal of Hazardous Materials B133: 226-232.

Chakrabarti, S. & Dutta, B.K. 2004. Photocatalytic degradation of model textile dyes in wastewater using ZnO as semiconductor catalyst. Journal of Hazardous Materials B112: 269-278.

Daneshvar, N., Rasoulifard, M.H., Khataee, A.R. & Hosseinzadeh, F. 2007. Removal of C.I. Acid Orange 7 from aqueous solution by UV irradiation in the presence of ZnO nanopowder. Journal of Hazardous Materials 143: 95-101.

Daneshvar, N., Salari, D. & Khataee, A.R. 2004. Photocatalytic degradation of azo dye acid red 14 in water on ZnO as an alternative catalyst to TiO2. Journal of Photochemistry and Photobiology A: Chemistry 162: 317-322.

Fotiadis, C., Xekoukoulotakis, N.P. & Mantzavinos, D. 2007. Photocatalytic treatment of wastewater from cottonseed processing: Effect of operating conditions, aerobic biodegradability and ecotoxicity. Catalysis Today 124: 247-253.

Gümüş, D. & Akbal, F. 2011. Photocatalytic degradation of textile dye and wastewater. Water Air Soil Pollution 216: 117-124.

Habibi, M.H. & Askari, E. 2011. Photocatalytic degradation of an azo textile dye with manganese-doped ZnO nanoparticles coated on glass. Iranian Journal of Catalysis 1: 41-44.

Hameed, B.H. & Ahmad, A.A. 2009. Batch adsorption of methylene blue from aqueous solution by garlic peel an agricultural waste biomass. Journal of Hazardous Materials 164: 870-875.

Kansal, S.K., Singh, M. & Sud, D. 2007. Studies on photodegradation of two commercial dyes in aqueous phase using different photocatalysts. Journal of Hazardous Materials 141(3): 581-590.

Kitture, R., Koppikar, S.J., Kaul-Ghanekar, R. & Kale, S.N. 2011. Catalyst efficiency, photostability and reusability study of ZnO nanoparticles in visible light for dye degradation. Journal of Physics and Chemistry of Solids 72: 60-66.

Krishnakumar, B. & Swaminathan, M. 2011. Influence of operational parameters on photocatalytic degradation of a genotoxic azo dye Acid Violet 7 in aqueous ZnO suspensions. Spectrochimica Acta Part A 81: 739-744.

Lin, W., Yan, X., Zhang, X., Qin, Z., Zhang, Z., Bai, Z., Lei, Y. & Zhang, Y. 2011. The comparison of ZnO nanowire detectors working under two wavelengths of ultraviolet. Solid State Communications 151: 1860-1863.

Lizama, C., Freer, J., Baeza, J. & Mansilla, H.D. 2002. Optimized photodegradation of Reactive Blue 19 on TiO2 and ZnO suspensions. Catalysis Today 76: 235-246.

Nishio, J., Tokumura, M., Znad, H.T. & Kawase, Y. 2006. Photocatalytic decolorization of azo-dye with zinc oxide powder in an external UV light irradiation slurry photoreactor. Journal of Hazardous Materials B138: 106-115.

Şahinkaya, S. 2013. COD and color removal from synthetic textile wastewater by ultrasound assisted electro-Fenton oxidation process. Journal of Industrial and Engineering Chemistry 19: 601-606.

Shinde, S.S., Shinde, P.S., Bhosale, C.H. & Rajpure, K.Y. 2011. Zinc oxide mediated heterogeneous photocatalytic degradation of organic species under solar radiation. Journal of Photochemistry and Photobiology B: Biology 104: 425- 433.

Sun, Q. & Yang, L. 2003. The adsorption of basic dyes from aqueous solution on modified peat-resin particle. Water Research 37: 1535-1544.

Tang, C. & Chen, V. 2004. The photocatalytic degradation of reactive black 5 using TiO2/UV in an annular photoreactor. Water Research 38: 2775-2781.

Tsang, D.C.W., Hu, J., Liu, M.Y., Zhang, W., Lai, K.C.K. & Lo, I.M.C. 2007. Activated carbon produced from waste wood pallets: Adsorption of three classes of dyes. Water Air Soil Pollution 184: 141-155.

Velmurugan, R. & Swaminathan, M. 2011. An efficient nanostructured ZnO for dye sensitized degradation of Reactive Red 120 dye under solar light. Solar Energy Materials & Solar Cells 95: 942-950.

Vineetha, M.N., Matheswaran, M. & Sheeba, K.N. 2013. Photocatalytic colour and COD removal in the distillery effluent by solar radiation. Solar Energy 91: 368-373.

Zhu, H., Jiang, R., Xiao, L., Chang, Y., Guan, Y., Li, X. & Zeng, G. 2009. Photocatalytic decolorization and degradation of Congo Red on innovative crosslinked chitosan/nano-CdS composite catalyst under visible light irradiation. Journal of Hazardous Materials 169: 933-940.

 

 

*Corresponding author; email: lnho@unimap.edu.my

 

 

 

previous