Sains Malaysiana 47(1)(2018): 169–179

http://dx.doi.org/10.17576/jsm-2018-4701-20

 

Effect of the Poly L-lactic Acid Coating on the Corrosion of Magnesium in Hank's Solution

(Kesan Salutan Acid L-laktik Poli ke atas Pengkakisan Magnesum dalam Larutan Hanks)

 

ATIKAH WAN NAFI*, AMALINA AFIFI, NOR ISHIDA ZAINAL ABIDIN, NOOR HIDAYAH ABDUL AZIZ & KATAYOON KALANTARI

 

Department of Mechanical Engineering, Faculty of Engineering, University of Malaya, 50603 Kuala Lumpur, Malaysia

 

Received: 21 March 2017/Accepted: 9 June 2017

 

ABSTRACT

To control the corrosion rate, the Magnesium (Mg) was coated with poly (l-lactic acid) (PLLA) using electrospinning technique. The effectiveness of the PLLA coating on the high purity Magnesium (HP Mg) and alloy AZ91 were tested in Hank's solution immersion test. The corrosion behaviour of Mg coated PLLA was studied through hydrogen evolution, weight loss and scanning electron microscope (SEM) before, during and after samples were immersed. The solution was maintained at pH 7 by bubbling CO2 gas. The results showed that surface treatment on Mg by coating with PLLA had reduced the rate of corrosion during the immersion test. The PLLA coating was also characterized and the coating adhesion was evaluated.

 

Keywords: Magnesium; SEM and PLLA coating; weight loss

 

ABSTRAK

Bagi mengawal kadar kakisan Magnesium; Mg disalut dengan asid (l-laktik) poli; PLLA menggunakan teknik putaran elektron. Keberkesanan PLLA yang membaluti HP Mg dan aloi AZ91 diuji dengan merendam di dalam cecair Hanks. Ciri-ciri kakisan oleh Mg bersalut PLLA dikenal pasti melalui pelepasan hidrogen, penurunan berat dan pengimbas mikroskop elektron (SEM) sebelum, semasa dan selepas sampel direndamkan. Cecair tersebut sentiasa berada pada pH 7 dengan aliran gas CO2. Keputusan menunjukkan bahawa kaedah rawatan kepada permukaan magnesium dengan disaluti PLLA telah menurunkan kadar kakisan semasa ujian rendaman. Salutan PLLA juga dikenal pasti dan kelekatan balutan juga diuji.

 

Kata kunci: Magnesium; penurunan berat; SEM dan salutan PLLA

REFERENCES

Abdalla, A.h., Barakat, N.A.M. & Lim, J.K. 2013. Influence of electrospinning and dip-coating techniques on the degradation and cytocompatibility of Mg-based alloy. Colloids and Surfaces A: Physicochemical and Engineering Aspects 42: 32-45.

Abdalla, A.h., Dewidar, M., Lim, J.H. & Lim, J.K. 2014. Enhanced biocorrosion resistance of surface modified magnesium alloys using inorganic/organic composite layer for biomedical application. Ceramics International 40(Issue 1, Part B): 2237-2247.

Abdalla, A.h., Dewidar, M. & Lim, J.K. 2012. Biocorrosion behavior and cell viability of adhesive polymer coated magnesium based alloys for medical implants. Applied Surface Science 261: 536-546.

Abdalla, A.h., Hwang, M.G. & Lim, J.K. 2012. In vitro bioactivity of titanium implants coated with bicomponent hybrid biodegradable polymers. J. Sol-Gel Sci. Technol. 64: 756-764.

Abidin, N.I.Z., Rolfe, B., Owen, H., Malisano, J., Martin, D., Hofstetter, J., Uggowitzer, P.J. & Atrens, A. 2013. The in vivo and in vitro corrosion of high-purity magnesium an

magnesium alloys WZ21 and AZ91. Corrosion Science 75: 354-366.

Agrawal, C. & Ray, R. 2001. Biodegrable polymeric scaffolds for musculoskeletal tissue engineering. J. Biomed. Mater. Res. 55: 141-150.

Amalina, M.A., Hajime, N., Hideki, Y., Yoshiharu, K. & Shigeyuki, N. 2009. Fabrication of aligned Poly(L-lactide) fibers by electrospinning and drawing. Macromolecular Materials and Engineering 294: 658-665.

Atrens, A., Liu, M. & Zainal Abidin, N.I. 2011. Corrosion mechanism applicable to biodegradable magnesium implants: A review. Materials Science and Engineering B 176: 1609- 1636.

Azad, A.M., McKelvey, S.L. & Al-Firdaus, Z. 2008. Fabrication of antimicrobial Titania nanofibers by electrospinning. The AMMTIAC Quarterly 3(3): 3-7. http://ammtiac.alionscience. com/quarterly.

Cao, F., Shi, Z., Song, G., Liu, M. & Atrens, A. 2013. Corrosion behaviour in salt spray and in 3.5% NaCl solution saturated with Mg(OH)2 of as-cast and solution heat-treated binary Mg-X alloys: X = Mn, Sn, Ca, Zn, Al, Zr, Si, Sr. Corrosion Science 76: 60-92.

Chen, X.N., Gu, Y.X., Lee, J.H., Lee, W.Y. & Wang, H.J. 2012. Multifunctional surfaces with biomimetic nanofibres and drug-eluting micro-patterns for infection control and bone tissue formation. European Cells and Materials 24: 237-248.

Chiu, K.Y., Wong, M.H., Cheng, F.T. & Man, H.C. 2007. Characterization and corrosion studies of fluoride conversion coating on degradable Mg implants. Surface & Coatings Technology 202: 590-598.

Chu, P.K., Chen, J.Y., Wang, L.P. & Huang, N. 2002. Plasma-surface modification of biomaterials. Materials Science and Engineering: R: Reports 36(5-6): 143-206.

Deitzel, J., Kleinmeyer, J., Harris, D. & Beck, T.N. 2001. The effect of processing variables on the morphology of electrospun nanofibers and textiles. Polymer 42: 261-272.

Doshi, J. & Reneker, D.H. 1995. Electrospinning process and applications of electrospun fibers. Journal of Electrostatics 35(2-3): 151-160.

Duan, Y., Wang, Z., Yan, W., Wang, S., Zhang, S. & Jia, J. 2007. Preparation of collagen-coated electrospun nanofibers by remote plasma treatment and their biological properties. J. Biomater. Sci. Polym. Ed. 18(9): 1153-1164.

Frenot, A. & Chronakis, I.S. 2003. Polymer nanofibers assembled by electrospinning. Current Opinion in Colloid & Interface Science 8(1): 64-75.

Gu, Y., Bandopadhyay, S., Chen C.-f., Ning, C. & Guo, Y. 2013. Long-term corrosion inhibition mechanism of microarc coated AZ31 Mg alloys for biomedical applications. Materials and Design 46: 66-75.

Hiromoto, S. 2015. Self-healing property of hydroxyapatite and octacalcium phosphate coaatings on pure magnesium and magnesium alloy. Corrosion Science 100: 284-294.

Iafisco, M., Foltran, I., Sabbatini, S., Tosi, G. & Roveri, N. 2011. Electrospun nanostructured fibers of collagen-biomimetic apatite on titanium alloy. Hindawi Publishing Corporation.

Krikorian, V. & Pochan, D.J. 2003. Poly (L-lactic)/layered silicate nanocomposite: Fabrication, characterization, and properties. Chem. Mater. 15: 4317-4324.

Shenoy, S.L., Bates, W.D., Frisch, H.L. & Wnek, G.E. 2005. Role of chain entanglements on fiber formation during electrospinning of polymer solutions: Good solvent, non-specific polymer-polymer interaction limit. Polymer 46(10): 3372-3384.

Liang, D., Hsiao, B.S. & Chu, B. 2007. Functional electrospun nanofibrous scaffolds for biomedical applications. Advanced Drug Delivery Reviews 59: 1392-1412.

Niu, J., Yuan, G., Liao, Y., Mao, L., Zhang, J., Wang, Y., Huang, F., Jiang, Y., He, Y. & Ding, W. 2013. Enhanced biocorrosion resistance and biocompatibility of degradable Mg-Nd-Zn-Zr alloy by brushite coating. Materials Science and Engineering C 33: 4833-4841.

Pandey, A., Pandey, G.C. & Aswath, P.B. 2008. Synthesis of polylactic acid-polyglycolic acid blends using microwave radiation. Journal of the Mechanical Behavior of Biomedical Materials 1(3): 227-233.

Qiao, Z., Shi, Z., Hort, N., Abidin, N.I.Z. & Atrens, A. 2012. Corrosion behaviour of a nominally high purity Mg ingot produced by permanent mould direct chill casting. Corrosion Science 61: 185-207.

Ravichandran, R. 2009. Biomimetic surface modification of dental implant for enhanced osseointegration. Tesis Master of Engineering, National University of Singapore, Singapore (Unpublished).

Razavi, M., Fathi, M., Savabi, O., Razavi, S.M., Beni, B.H., Vashaee, D. & Tayebi, L. 2014. Controlling the degradation rate of bioactive magnesium implants by electrophoretic deposition of akermanite coating. Ceramics International 40: 3865-3872.

Rojaee, R., Fathi, M. & Raeissi, K. 2013. Controlling the degradation rate of AZ91 magnesium alloy via sol-gel derived nanostructured hydroxyapatite coating. Materials Science and Engineering C 33: 3817-3825.

Rojaee, R., Fathi, M. & Raeissi, K. 2013. Electrophoretic deposition of nanostructured ydroxyapatite coating on AZ91 magnesium alloy implants with different surface treatments. Applied Surface Science 285P: 664-673.

Shah, P.N., Manthe, R.I., Lopina, S.T. & Yun, Y.H. 2009. Electrospinning of L-tyrosine polyurethanes for biomedical applications. Polymer 50(10): 2281-2289.

Shi, Z. & Atrens, A. 2011. An innovative specimen configuration for the study of Mg corrosion. Corrosion Science 53: 226-246.

Song, G. 2007. Control of biodegradation of biocompatable magnesium alloys. Corrosion Science 49(4): 1696-1701.

Staiger, M.P., Pietak, A.M., Huadmai, J. & Dias, G. 2006. Magnesium and its alloys as orthopedic biomaterials: A review. Biomaterials 27(9): 1728-1734.

Virtanen, S. 2011. Biodegradable Mg and Mg alloys: corrosion and biocompatibility: A review. Materials science and Engineering B 176: 1600-1608.

Wen, C., Guan, S., Peng, L., Ren, C., Wang, X. & Hu, Z. 2009. Characterizatian and degradation behavior of AZ31 alloy surface modified by bone-like hydroxypatite for implant application. Applied Surface Science 255(13-14): 6433-6438.

Wong, H.M., Yeung, K.W.K. Lam, K.O., Tam, V., Chu, P.K., Luk, K.D.K. & Cheung, K.M.C. 2010. A biodegradable polymer-based coating to control the performance of magnesium alloy orthopaedic implants. Biomaterials 31(8): 2084-2096.

Yamamoto, A. & Hiromoto, S. 2009. Effect of inorganic salts, amino acids and proteins on the degradation of pure magnesium in vitro. Materials Science and Engineering C 29: 1559-1568.

Zainal Abidin, N.I., Forno, A.D., Bestetti, M., Martin, D., Beer, A. & Atrens, A. 2015. Evaluation of coating for Mg Alloys for biomedical applications. Advanced Engineering Materials 17: 58-67.

Zainal Abidin, N.I., Atrens, A.D., Martin, D. & Atrens, A. 2011. Corrosion of high purity Mg, Mg2Zn0.2Mn, ZE41 and AZ91 in Hank's solution at 37'C. Corrosion Science 53: 3542-3556.

Zainal Abidin, N.I., Martin, D. & Atrens, A. 2011. Corrosion of high purity Mg, AZ91, ZE41 and Mg2Zn0.2Mn in Hank's solution at room temperature. Corrosion Science 53: 862-872.

Zhang, R. & Ma, P.X. 1998. Porous poly(L-lactic acid)/apatite composites created by biomimetic process. J. Biomed. Mater. Res. 45(4): 285-293.

Zhao, L., Liu, Q., Wang, J., Yang, W. & Liu, L. 2014. One-step method for the fabrication of superhydrophobic surface on magnesium alloy and its corrosion protection, antifouling performance. Corrosion Science 80: 177-183.

Zhao, M.C., Liu, M., Song, G. & Atrens, A. 2008. Influence of the B-phase morphology on the corrosion of the mg alloy AZ91. Corrosion Science 50: 1939-1953.

Zhao, M.C., Schmutz, P., Brunner, S., Liu, M., Song, G. & Atrens, A. 2009. An exploratory study of the corrosion of mg alloys during interrupted salt spray testing. Corrosion Science 51: 1277-1292.

 

 

*Corresponding author; email: Atikah_nafi@yahoo.com

 

 

 

 

previous