Sains Malaysiana 45(8)(2016): 1207–1211

Fabrication of Flourine Doped Tin Oxide with Different Volume of Solvents on FTO Seed Layer by Hydrothermal Method

(Fabrikasi Flourin Terdop Timah Oksida dengan Jumlah Pelarut Berbeza ke atas Lapisan Benih FTO melalui Kaedah Hidroterma)

 

M.L. MOHD NAPI*, N. NAYAN, M.K. AHMAD, F.I.M. FAZLEE, N.K.A. HAMED

& N.S. KHALID

 

Microelectronics and Nanotechnology, Shamsuddin Research Centre (MiNT- SRC), Universiti Tun Hussein Onn Malaysia, 86400 Batu Pahat, Johor Darul Takzim, Malaysia

 

Diserahkan: 20 April 2015/Diterima: 18 November 2015

 

ABSTRACT

Flourine doped tin oxide films were synthesized by using hydrothermal method with different volume of solvents. The thin film growth was carried out by fixing the concentration of tin and fluorine element precursors by only varying their solvents which were 2-propanol and DI water. The fabrication of FTO thin film by using mineral salt group as tin precursor with hydrothermal method on soda lime glass showed that the nanostructured growth did not distribute largely and took longer time. The seed layer of FTO has been used to overcome these problems thus the thin film growth distributed largely in short time. These experiments were conducted at a constant of hydrothermal temperature and reaction time which were 150°C and 5 h respectively. The result showed that, there was a change on the surface morphology in the formation of FTO films. The minimum value of sheet resistance was 0.1475 Ω/sq which was obtained using 65 mL of 2-propanol and 20 mL of DI water was lower than sheet resistance of commercial FTO films of 01693 Ω/sq. This fabricated FTO films showed a good transparency with higher of transmittance than 80%. The experimental findings suggested that 65 mL amount of 2-propanol and 20 mL of DI water in precursor solutions could produce the better of FTO performance than commercial FTO.

 

Keywords: Electrical properties; hydrothermal method; nanoparticle; thin film; water

 

ABSTRAK

Flourin terdop timah oksida telah disintesis menggunakan kaedah hidroterma dengan pelbagai jumlah isi padu pelarut. Pertumbuhan filem nipis dijalankan dengan mengekalkan kepekatan unsur timah dan flourin dengan hanya mengubah isi padu pelarut iaitu 2-propanol dan air suling. Fabrikasi filem nipis FTO dengan menggunakan kaedah hidroterma di atas sampel kaca kosong telah menunjukkan bahawa pertumbuhan struktur nano tidak menyeluruh dan mengambil masa yang lama. Lapisan benih FTO telah digunakan untuk mengatasi masalah ini seterusnya menghasilkan pertumbuhan filem nipis yang menyeluruh dalam masa yang singkat. Penyelidikan ini dijalankan dengan mengekalkan suhu hidroterma iaitu 150°C selama 5 jam bagi tempoh reaksi. Hasil kajian menunjukkan terdapat perubahan pada sifat permukaan bagi pembentukan filem nipis FTO. Nilai rintangan minimum helaian ialah 0.1475 Ω/sq yang diperoleh dengan menggunakan isi padu pelarut sebanyak 65 mL 2-propanol dan 20 mL air ternyahion yang lebih rendah nilainya jika dibandingkan dengan nilai rintangan helaian bagi FTO komersial iaitu sebanyak 0.1693 Ω/sq. Filem nipis FTO yang difabrikasi ini menunjukkan sifat kelutsinaran yang baik iaitu nilai kepancaran yang lebih tinggi daripada 80%. Hasil kajian mencadangkan bahawa dengan menggunakan 65 mL 2-propanol dan 20 mL air ternyahion dalam larutan pelopor boleh menghasilkan perilaku FTO yang lebih baik berbanding FTO komersial.

 

Kata kunci: Air; filem nipis; kaedah hidroterma; sifat elektrik; zarah nano


RUJUKAN

 

Batzill, M. & Diebold, U. 2005. The surface and materials science of tin oxide. Progress in Surface Science 79(2): 47-154.

Chen, Z.W., Lai, J.K.L. & Shek, C.H. 2005. Multifractal spectra of scanning electron microscope images of SnO2 thin films prepared by pulsed laser deposition. Physics Letters A 345(1): 218-223.

Ciddor, P.E. 1996. Refractive index of air: new equations for the visible and near infrared. Applied Optics 35(9): 1566-1573.

Dou, X., Sabba, D., Mathews, N., Wong, L.H., Lam, Y.M. & Mhaisalkar, S. 2011. Hydrothermal synthesis of high electron mobility Zn-doped SnO2 nanoflowers as photoanode material for efficient dye-sensitized solar cells. Chemistry of Materials 23(17): 3938-3945.

Fang, T.H. & Chang, W.J. 2003. Effect of freon flow rate on tin oxide thin films deposited by chemical vapor deposition. Applied Surface Science 220(1): 175-180.

Ghafouri, V., Shariati, M. & Ebrahimzad, A. 2012. Photoluminescence investigation of crystalline undoped ZnO nanostructures constructed by RF sputtering. Scientia Iranica 19(3): 934-942.

Gordon, R.G. 2000. Criteria for choosing transparent conductors. MRS bulletin 25(08): 52-57.

Kong, J., Deng, H., Yang, P. & Chu, J. 2009. Synthesis and properties of pure and antimony-doped tin dioxide thin films fabricated by sol-gel technique on silicon wafer. Materials Chemistry and Physics 114(2): 854-859.

Mohd Khairul bin Ahmad & Murakami, K. 2012. Low temperature and normal pressure growth of rutile-phased TiO2 nanorods/nanoflowers for DSC application prepared by hydrothermal method. Journal of Advanced Research in Physics 3(2): 021208.

Moholkar, A.V., Pawar, S.M., Rajpure, K.Y., Almari, S.N., Patil, P.S. & Bhosale, C.H. 2008. Solvent-dependent growth of sprayed FTO thin films with mat-like morphology. Solar Energy Materials and Solar Cells 92(11): 1439-1444.

Moholkar, A.V., Pawar, S.M., Rajpure, K.Y. & Bhosale, C.H. 2007. Effect of solvent ratio on the properties of highly oriented sprayed fluorine-doped tin oxide thin films. Materials Letters 61(14): 3030-3036.

Premalal, Edirisinghage V.A, Dematage, N., Kaneko, S. & Konno, A. 2012a. Development of quality FTO films by spray pyrolysis for dye-sensitized solar cell. Electrochemistry 80(9): 624-628.

Premalal, EVA, N. Dematage, S. Kaneko & A Konno. 2012b. Preparation of high quality spray-deposited fluorine-doped tin oxide thin films using dilute di (n-butyl) tin (iv) diacetate precursor solutions. Thin Solid Films 520(22): 6813-6817.

Samad, Wan Zurina, Muhamad Mat Salleh, Ashkan Shafiee, and Mohd Ambar Yarmo. 2011. Structural, optical and electrical properties of fluorine doped tin oxide thin films deposited using inkjet printing technique. Sains Malaysiana 40(3): 251-257.

Saturi Baco, Abdullah Chik & Fouziah Md Yassin. 2012. Study on optical properties of tin oxide thin film at different annealing temperature. Journal of Science and Technology 4(1): 61-72.

Smith, Agnes, Jean-Marc Laurent, David S Smith, and Jean Pierre Bonnet. 1998. Experimental survey of different precursor/ solvent pairs for the deposition of tin dioxide by pyrosol. Thin Solid Films 315(1): 17-21.

Wang, H., Fang Fu, Feihu Zhang, Hong-En Wang, Stephen V. Kershaw, Jiaqiang Xu, Shi-Gang Sun, and Andrey L. Rogach. 2012. Hydrothermal synthesis of hierarchical SnO2 microspheres for gas sensing and lithium-ion batteries applications: Fluoride-mediated formation of solid and hollow structures. Journal of Materials Chemistry 22(5): 2140-2148.

Wang, H., Kalytchuk, S., Yang, H., He, L., Hu, C., Teoh, W.Y. & Rogach, A.L. 2014. Hierarchical growth of SnO2 nanostructured films on FTO substrates: structural defects induced by Sn (II) self-doping and their effects on optical and photoelectrochemical properties. Nanoscale 6(11): 6084-6091.

Wu, S., Yuan, S., Shi, L., Zhao, Y. & Fang, J. 2010. Preparation, characterization and electrical properties of fluorine-doped tin dioxide nanocrystals. Journal of Colloid and Interface Science 346(1): 12-16.

Yadav, A.A., Masumdar, E.U., Moholkar, A.V., Rajpure, K.Y. & Bhosale, C.H. 2009. Effect of quantity of spraying solution on the properties of spray deposited fluorine doped tin oxide thin films. Physica B: Condensed Matter 404(12): 1874-1877.

Zhao, H., Liu, Q., Cai, Y. & Zhang, F. 2008. Effects of water on the structure and properties of F-doped SnO2 films. Materials Letters 62(8-9): 1294-1296.

 

 

*Pengarang untuk surat menyurat; email: mluqmannapi@gmail.com

 

 

 

sebelumnya