Sains Malaysiana 47(7)(2018): 1547–1556

http://dx.doi.org/10.17576/jsm-2018-4707-24

 

Sintesis MnO₂ Lapisan Nipis Poros menggunakan Templat Silika Alumina-Aptes: Aplikasi Penjerapan Pewarna

(Synthesis of Porous Thin Layer MnO₂ using Silica Alumina - Aptes Template: Application of Dyes Adsorption)

 

SITI ZUBAIDAH HASAN¹, ZUHAILIE ZAKARIA¹, MOHAMED ROZALI OTHMAN^1,2*

& MUHAMMAD RAHIMI YUSOP¹

 

¹School of Chemical Science and Food Technology, Faculty of Science and Technology, Universiti Kebangsaan Malaysia, 43600 UKM Bangi, Selangor Darul Ehsan, Malaysia

 

²Centre for Water Research and Analysis, Faculty of Science and Technology, Universiti Kebangsaan Malaysia, 43600 UKM Bangi, Selangor Darul Ehsan, Malaysia

 

Diserahkan: 8 November 2017/Diterima: 14 Februari 2018

 

ABSTRAK

Mangan oksida (MnO₂) poros nano yang mempunyai morfologi lapisan nipis telah disintesis dan diaplikasikan sebagai penjerap pewarna sintetik komersial (remazol merah, eriokrom hitam dan metilena biru). Permukaan bahan silika alumina yang telah diubah suai dengan 3-aminopropiltrietoksisilana (APTES) digunakan dalam proses sonokimia pada suhu bilik dengan kehadiran 0.1 M kalium permanganat (KMnO₄) untuk menghasilkan komposit silika alumina-MnO₂. Penyingkiran templat dijalankan untuk mendapatkan MnO₂ tulen bersaiz nano. Spektrum FTIR menunjukkan kehadiran getaran MnO₂ dalam julat 400 - 600 cm^-1 dan corak XRD menunjukkan kehadiran birnesit jenis MnO₂. Isoterma jerap-nyahjerap N₂ menunjukkan MnO₂ tulen memiliki liang yang bersifat mesoporos iaitu 34.8 Å (± 0.4), manakala luas permukaan MnO₂ ialah 252.8 m₂/g. Penjerap MnO₂ lapisan nipis yang diperoleh menunjukkan kebolehan menjerap pewarna eriokrom hitam dan metilena biru masing-masingnya sehingga 54% dan 99% serta kapasiti penjerapan masing-masing ialah 0.0024 dan 0.0077 mmol/g. Kedua-dua isoterma penjerapan eriokrom hitam dan metilena biru oleh MnO₂ masing-masing menepati ciri-ciri Langmuir dan Temkin. Sementara itu data kinetik penjerapan eriokrom hitam dan metilena biru kedua-duanya memenuhi tertib pertama pseudo.

 

Kata kunci: Jerapan; logam oksida; sonokimia

 

ABSTRACT

Nanoporous manganese oxide (MnO₂) with thin layer morphology has been synthesized and applied as commercial synthetic dye absorbent (remazol red, eriochrome black and methylene blue). The modified surface alumina silica with 3-aminopropyltriethoxysilane (APTES) is used in the sonochemical process at room temperature with the presence of 0.1 M potassium permanganate (KMnO₄) to produce alumina silica-MnO₂ composite. Template removal is performed to get pure nanosized MnO₂. The FTIR spectrum shows the presence of MnO₂ vibrations in the range of 400 - 600 cm-1 and XRD pattern shows the presence of MnO₂-birnessite. The N₂ adsorption-desorption isotherm shows that pure MnO₂ has a mesoporous pore of 34.8 Å (± 0.4), while the surface area is 252.8 m₂/g. The nanosized MnO₂ with thin layer morphology obtained shows the ability to absorb eriochrome black and methylene blue dyes with the value of 54% and 99% and adsorption capacity of 0.0024 and 0.0077 mmol/g, respectively. Both the adsorption isotherm of eriochrome black and methylene blue by MnO₂ meets the characteristics of Langmuir and Temkin, respectively. Meanwhile, kinetic adsorption of both eriochrom black and methylene blue meets the characteristics of pseudo first order.

 

Keywords: Adsorption; metal oxide; sonochemical

RUJUKAN

Abdullah, A.H. & Wong, W.Y. 2010. Decolorization of reactive orange 16 dye by copper oxide system. Sains Malaysiana 39(4): 587-591.

Antony, R., David Manickam, S.T., Kollu, P., Chandrasekar, P.V., Karuppasamy K. & Balakumar, S. 2014. Highly dispersed Cu(II), Co(II) and Ni(II) catalysts covalently immobilized on imine-modified silica for cyclohexane oxidation with hydrogen peroxide. RSC Advances 4: 24820-24830.

Asouhidou, D.D., Triantafyllidis, K.S., Lazaridis, N.K. & Matis, K.A. 2009. Adsorption of remazol red 3BS from aqueous solutions using aptes- and cyclodextrin-modified HMS-type mesoporous silicas. Colloids and Surfaces A: Physicochemical and Engineering Aspects 346: 83-90.

Asouhidou, D.D., Triantafyllidis, K.S., Lazaridis, N.K. & Matis, K.A. 2012. Adsorption of reactive dyes from aqueous solutions by layered double hydroxides. Journal of Chemical Technology & Biotechnology 87: 575-582.

Basila, M.R. & Kantner, T.R. 1967. Infrared spectrum of ammonia adsorbed on silica-alumina. The Journal of Physical Chemistry 71: 467-472.

Cao, J., Mao, Q., Shi, L. & Qian, Y. 2011. Fabrication of γ-MnO₂/ α-MnO₂ hollow core/shell structures and their application to water treatment. Journal of Materials Chemistry 21: 16210-16215.

Chen, H. & He, J. 2008. Facile synthesis of monodisperse manganese oxide nanostructures and their application in water treatment. The Journal of Physical Chemistry C 112: 17540-17545.

Chen, R., Yu, J. & Xiao, W. 2013. Hierarchically porous MnO₂ microspheres with enhanced adsorption performance. Journal of Materials Chemistry A. 1: 11682-11690.

Cui, H.J., Huang, H.Z., Yuan, B. & Fu, M.L. 2015. Decolorization of Rhb dye by manganese oxides: effect of crystal type and solution ph. Geochemical Transactions 16: 10.

Dada, A., Olalekan, A., Olatunya, A. & Dada, O. 2012. Langmuir, Freundlich, Temkin and Dubinin–Radushkevich isotherms studies of equilibrium sorption of Zn²⁺ unto phosphoric acid modified rice husk. Journal of Applied Chemistry 3: 38-45.

Fei, J., Cui, Y., Yan, X., Qi, W., Yang, Y., Wang, K., He, Q. & Li, J. 2008. Controlled preparation of MnO2 hierarchical hollow nanostructures and their application in water treatment. Advanced Materials-Deerfield Beach Then Weinheim 20: 452.

Ge, J. & Qu, J. 2003. Degradation of azo dye acid Red B on manganese dioxide in the absence and presence of ultrasonic irradiation. Journal of Hazardous Materials 100: 197-207.

Hasan, S.Z., Yusop, M.R. & Othman, M.R. 2015. Sintesis amorfus mangan dioksida (MnO₂) nano-poros menggunakan proses sonokimia dan bukan sonokimia. Malaysian Journal of Analytical Sciences 19: 388-396.

Ho, Y.S. & Mckay, G. 1999. Pseudo-second order model for sorption processes. Process Biochemistry 34: 452-465.

Huang, M., Zhang, Y., Li, F., Zhang, L., Ruoff, R.S., Wen, Z. & Liu, Q. 2014. Self-assembly of mesoporous nanotubes assembled from interwoven ultrathin birnessite-type MnO₂ nanosheets for asymmetric supercapacitors. Scientific Reports 4: 3878.

Kyzas, G.Z., Fu, J. & Matis, K.A. 2013. The change from past to future for adsorbent materials in treatment of dyeing wastewaters. Materials 6: 5131-5158.

Manning, B.W., Cerniglia, C.E. & Federle, T.W. 1985. Metabolism of the benzidine-based azo dye direct black 38 by human intestinal microbiota. Applied and Environmental Microbiology 50: 10-15.

Nony, C.R. & Bowman, M.C. 1980. Trace analysis of potentially carcinogenic metabolites of an azo dye and pigment in hamster and human urine as determined by two chromatographic procedures. Journal of Chromatographic Science 18: 64-74.

Pang, Y.L. & Abdullah, A.Z. 2013. Current status of textile industry wastewater management and research progress in Malaysia: A Review. CLEAN - Soil, Air, Water 41: 751-764.

Paz, D.S., Baiotto, A., Schwaab, M., Mazutti, M., Bassaco, M., Bertuol, D., Foletto, E. & Meili, L. 2013. Use of papaya seeds as a biosorbent of methylene blue from aqueous solution. Water Science and Technology 68: 441-447.

Robinson, T., Mcmullan, G., Marchant, R. & Nigam, P. 2001. Remediation of dyes in textile effluent: A critical review on current treatment technologies with a proposed alternative. Bioresource Technology 77: 247-225.

Ryu, S.H., Hwang, S.G., Yun, S.R., Cho, K.K., Kim, K.W. & Ryu, K.S. 2011. Synthesis and electrochemical characterization of silica-manganese oxide with a core-shell structure and various oxidation states. Bulletin of the Korean Chemical Society 32: 2683.

Salleh, M.A.M., Mahmoud, D.K., Karim, W.A.W.A. & Idris, A. 2011. Cationic and anionic dye adsorption by agricultural solid wastes: A comprehensive review. Desalination 280: 1-13.

Santos, D.O., Nascimento Santos, M.d.L., Santana Costa, J.A., de Jesus, R.A., Navickiene, S., Sussuchi, E.M. & de Mesquita, M.E. 2013. Investigating the potential of functionalized MCM-41 on adsorption of remazol red dye. Environmental Science and Pollution Research 20(7): 5028-5035.

Sing, K.S. 1985. Reporting physisorption data for gas/solid systems with special reference to the determination of surface area and porosity (Recommendations 1984). Pure and Applied Chemistry 57: 603-619.

Zhu, J., Shi, W., Xiao, N. Rui, X., Tan, H., Lu, X., Hng, H.H., Ma, J. & Yan, Q. 2012. Oxidation-etching preparation of MnO₂ tubular nanostructures for high-performance supercapacitors. ACS Applied Materials & Interfaces 45: 2769-2774.

Zhu, S., Zhou, Z., Zhang, D. & Wang, H. 2006. Synthesis of mesoporous amorphous MnO₂ from SBA-15 via surface modification and ultrasonic waves. Microporous and Mesoporous Materials 95: 257-264.

 

*Pengarang untuk surat-menyurat; email: rozali@ukm.edu.my