Sains Malaysiana 49(12)(2020): 3045-3054

http://dx.doi.org/10.17576/jsm-2020-4912-16

 

Effect of Isothermal Aging and Copper Substrate Roughness on the SAC305 Solder Joint Intermetallic Layer Growth of High Temperature Storage (HTS)

(Kesan Penuaan Isoterma dan Kekasaran Permukaan Substrat Kuprum ke atas Pertumbuhan Lapisan antara Logam Sambungan Pateri SAC305 pada Penyimpanan Suhu Tinggi (HTS))

 

RABIAH AL ADAWIYAH AB RAHIM1, MUHAMMAD NUBLI ZULKIFLI2, AZMAN JALAR1,3*, ATIQAH MOHD AFDZALUDDIN1 & KIM SIOW SHYONG1

 

1Institute of Microengineering and Nanoelectronics (IMEN), Universiti Kebangsaan Malaysia, 43600 UKM Bangi, Selangor Darul Ehsan, Malaysia

 

2Universiti Kuala Lumpur (UniKL), British Malaysia Institute (BMI), Electrical Engineering Section, Jalan Sungai Pusu, 53100 Gombak, Selangor Darul Ehsan, Malaysia


3Department of Applied Physics, Faculty of Science & Technology, Universiti Kebangsaan Malaysia, 43600 UKM Bangi, Selangor Darul Ehsan, Malaysia

 

Diserahkan: 13 Ogos 2020/Diterima: 27 Ogos 2020

 

ABSTRACT

This study aims to evaluate the effect of copper (Cu) substrate surface roughness on the intermetallic compound (IMC) growth and interfacial reaction of SAC305 lead-free solder joint after undergone an aging process. Aging process was conducted using high temperature storage (HTS) at temperature of 150 °C and aging times of 200, 400, 600, 800, and 1000 h. IMC morphology and growth were examined using infinite focus microscope (IFM). Then, the SAC305 solder joint IMC growth kinetic was measured based on power law relationship and diffusion coefficient formula. It was noted that the morphology of IMC for the rougher Cu substrate has scallop-shaped and uniform layer as compared to that of smoother Cu substrate for the initial exposure to the HTS. In addition, Cu substrate with Ra of 579 nm is the turning point for the creation of Cu6Sn5 towards more Cu3Sn of IMC. In addition, Cu substrate with Ra of 579 nm also acts as the turning point for the IMC growth of SAC305 solder joint on Cu substrate for the solid-state diffusion to be happened during 150 °C of aging from grain boundary dominant toward volume diffusion dominant.

 

Keywords: High temperature storage (HTS); IMC layer growth, IMC thickness; SAC305 solder; substrate roughness

 

ABSTRAK

Kajian ini bertujuan untuk menilai kesan kekasaran permukaan substrat kuprum (Cu) ke atas pertumbuhan lapisan sebatian antara logam (IMC) dan tindak balas antara muka sambungan pateri SAC305 selepas melalui proses penuaan. Proses penuaan dijalankan menggunakan penyimpanan suhu tinggi (HTS) pada suhu 150 °C dan masa penuaan 200, 400, 600, 800 dan 1000 jam. Morfologi dan pertumbuhan IMC dicerap menggunakan mikroskop fokus tak terjangka (IFM). Kemudian, pertumbuhan kinetik sambungan pateri SAC305 diukur berdasarkan hubungan hukum kuasa dan formula pekali resapan. Morfologi IMC untuk substrat Cu yang lebih kasar menunjukkan ia berbentuk kerangan dan lapisan yang seragam berbanding substrat Cu yang lebih licin untuk permulaan pendedahan kepada HTS. Sebagai tambahan, substrat Cu dengan 579 nm Ra merupakan titik permulaan kepada pertumbuhan IMC sambungan pateri SAC305 di atas substrat Cu untuk resapan keadaan pepejal berlaku semasa penuaan 150 °C daripada dominan sempadan terhadap dominan resapan isi padu.

 

Kata kunci: Kekasaran substrat; ketebalan IMC; penyimpanan suhu tinggi (HTS); pertumbuhan lapisan IMC; pateri SAC305

 

RUJUKAN

Abu Bakar, M., Azman, J., Roslina, I. & Abdul, R.D. 2016. Nanoindentation of Sn3Ag0. 5Cu/ENIG solder joint after high temperature storage. Materials Science Forum 857: 40-43.

Anon. N.D.R. 2020. RMS Surface Roughness Calculation - Surface Finish Formulas, Harrison Electropolishing. http://www.harrisonep.com/electropolishing-ra.html. Accessed on 26 August 2020.

Bhat, K.N., Prabhu, K.N. & Satyanarayan. 2014. Effect of reflow temperature and substrate roughness on wettability, IMC growth and shear strength of SAC387/Cu bonds. Journal of Materials Science: Materials in Electronics 25(2): 864-872.

Hu, X., Xu, T., Keer, L.M., Li, Y. & Jiang, X. 2016. Microstructure evolution and shear fracture behavior of aged Sn3Ag0.5Cu/Cu solder joints. Materials Science and Engineering: A 673: 167-177.

Ismail, N., Jalar, A., Abu Bakar, M. & Ismail, R. 2018a. Kesan penambahan tiubnano karbon terhadap pertumbuhan lapisan sebatian antara logam sistem pateri Sn-Ag-Cu/Cu akibat penuaan terma. Sains Malaysiana 47(7): 1585-1590.

Ismail, N., Ismail, R., Jalar, A., Omar, G., Salleh, E.M., Kamil, N. & Rahman, I.A. 2018b. Comparative study of interfacial interaction between aromatic and aliphatic functional group in solder wettability. Journal of Materials Science: Materials in Electronics 29(15): 12910-12916.

Ismail, N., Ismail, R., Nik Ubaidillah, N.K.A., Jalar, A. & Zain, N.M. 2016a. Surface roughness and wettability of SAC/CNT lead free solder. Materials Science Forum 857: 73-75.

Ismail, N., Ismail, R., Abd Aziz, N.I. & Jalar, A. 2016b. Wettability of CNT-doped solder under isothermal aging. Materials Science Forum 857: 76-78.

Jalar, A., Abu Bakar, M., Ismail, R. & Abdul, R.D. 2016. Statistical aspect on the measuring of intermetallic compound thickness of lead free solders. Journal of Scientific Research and Development 3(4): 49-54.

Jiang, N., Zhang, L., Liu, Z-Q., Sun, L., Long, W-M., He, P., Xiong, M-Y. & Zhao, M. 2019. Reliability issues of lead-free solder joints in electronic devices. Science and Technology of Advanced Materials 20(1): 876-901.

Lee, J-H. & Kim, Y-J. 2014. Hydroxyapatite nano fibers fabricated through electrospinning and sol-gel process. Ceramics International 40(2): 3361-3369.

Lee, L.M. & Ahmad, A.M. 2013. Interfacial reaction of Sn-Ag-Cu lead-free solder alloy on Cu: A review. Advances in Materials Science and Engineering 2013: Article ID. 123697.

Li, H., An, R., Wang, C. & Jiang, Z. 2015. In situ quantitative study of microstructural evolution at the interface of Sn3.0Ag0.5Cu/Cu solder joint during solid state aging. Journal of Alloys and Compounds 634: 94-98.

Liu, J., Zhao, H., Li, Z., Song, X., Zhao, Y., Niu, H., Tian, H., Dong, H. & Feng, J. 2018. Microstructure evolution, grain morphology variation and mechanical property change of Cu-Sn intermetallic joints subjected to high-temperature aging. Materials Characterization 135(November): 238-244.

Mo, L., Wu, F. & Liu, C. 2015. Growth kinetics of IMCs in Cu-Sn intermetallic joints during isothermal soldering process. Proceedings - Electronic Components and Technology Conference. pp. 1854-1858.

Rabiatul Adawiyah, M.A. & Saliza Azlina, O. 2018. Comparative study on the isothermal aging of bare Cu and ENImAg surface finish for Sn-Ag-Cu solder joints. Journal of Alloys and Compounds 740: 958-966.

Satyanarayan & Prabhu, K.N. 2013. Spreading behavior and evolution of IMCs during reactive wetting of sac solders on smooth and rough copper substrates. Journal of Electronic Materials 42(8): 2696-2707.

Tang, Y., Luo, S.M., Li, Z.H., Hou, C.J. & Li, G.Y. 2018. Morphological evolution and growth kinetics of interfacial Cu 6 Sn 5 and Cu 3 Sn layers in low-Ag Sn-0.3 Ag-0.7 Cu-XMn/Cu solder joints during isothermal ageing. Journal of Electronic Materials 47(10): 5913-5929.

Wang, C., Li, M., Chiu, C. & Chang, T. 2018. Kinetic study of solid-state interfacial reactions of p-type (Bi, Sb) 2Te3 thermoelectric materials with Sn and Sn–Ag–Cu solders. Journal of Alloys and Compounds 767: 1133-1140.

Wang, Y., Wang, G., Song, K. & Zhang, K. 2017. Effect of Ni addition on the wettability and microstructure of Sn2.5Ag0.7Cu0.1RE solder alloy. Materials & Design 119: 219-224.

Wu, Y., Jennifer, A.S., Cyrus, P., Ann Foster, L., Marshall, J.L., Jacobs, E.G. & Pinizzotto, R.F. 1993. The formation and growth of intermetallics in composite solder. Journal of Electronic Materials 22(7): 769-777.

Xiao, H., Li, X.Y., Zhu, Y.X., Yang, J.L., Chen, J. & Guo, F. 2013. Intermetallic growth study on SnAgCu/Cu solder joint interface during thermal aging. Journal of Materials Science: Materials in Electronics 24(7): 2527-2536.

Yang, M., Ko, Y-H., Bang, J., Kim, T-S., Lee, C-W. & Li, M. 2017. Effects of Ag addition on solid–state interfacial reactions between Sn–Ag–Cu solder and Cu substrate. Materials Characterization 124: 250-259.

Yu, D.Q., Wu, C.M.L., Law, C.M.T., Wang, L. & Lai, J.K.L. 2005. Intermetallic compounds growth between Sn-3.5Ag lead-free solder and Cu substrate by dipping method. Journal of Alloys and Compounds 392(1-2): 192-199.

Zhu, Z., Ma, H., Shang, S., Ma, H., Wang, Y. & Li, X. 2019. Effect of polycrystalline Cu microstructures on IMC growth behavior at Sn/Cu soldering interface. Journal of Materials Science: Materials in Electronics 30(17): 15964-15971.

 

*Pengarang untuk surat-menyurat; email: azmn@ukm.edu.my

   

 

sebelumnya