Microstructural Properties of Semisolid Welded Joints for AISI D2 Tool Steel
M.N. Mohammed, M. Z. Omar, J. Syarif, Z. Sajuri, M. S. Salleh, K. S. Alhawari
Corresponding author (email) : mohammed.ukm@gmail.com
Abstract
The aim of this study is to investigate experimentally the microstructural evolution of the joints using ledeburitic AISI D2Tool Steel parts. The application of a new process of the semisolid joining of two parts of AISI D2 cold-work tool steelis proposed using a partial remelting method. Samples were heated in an argon atmosphere up to 1300°C and held for10 minutes. Metallographic analyses along the joint interface showed a smooth transition from one to the other andneither oxides nor microcracking was observed. The current work successfully confi rmed that avoidance of a dendriticmicrostructure in the semisolid joined zone and high bonding quality components can be achieved without the need forforce or complex equipment when compared to conventional welding processes.
Keywords : Thixo-joining; direct partial re-melting; cold-work tool steel
Abstrak
Kajian ini dijalankan bertujuan untuk menyelidik secara eksperimen tentang evolusi mikrostruktur yang berlaku pada sambungan keluli perkakas ledubritik AISI D2. Penggunaan proses baharu untuk menyambungkan dua bahagian keluliperkakas kerja-sejuk AISI D2 dicadangkan dengan menngunakan kaedah pemanasan separa. Sampel dipanaskan di dalam atmosfera argon sehingga 1300°C selama 10 minit. Analisis metalografi sepanjang permukaan sambungan menujukkanperalihan yang rata daripada satu sama lain dan tiada berlaku pengoksidaan ataupun keretakan mikro yang kelihatan.Kajian ini berjaya mengesahkan pengelakan mikrostruktur dendritik di kawasan zon sambungan separa pepejal dankomponen mempunyai kualiti ikatan yang tinggi boleh dicapai tanpa memerlukan daya dan perkakasan yang kompleksjika dibandingkan dengan proses kimpalan konvensional.
Kata kunci: Sambungan-tikso; pemanasan separa pepajal; keluli perkakas kerja-sejuk