Sains Malaysiana 39(4)(2010): 593–598

 

Properties of Magnetic Paper Prepared via in situ Synthesis Method

(Sifat Kertas Bermagnet Disediakan Melalui Teknik Sintesis in situ)

 

Rose Farahiyan Munawar*, Sarani Zakaria, Shahidan Radiman

Chia Chin Hua & Mustaffa Abdullah

School of Applied Physics, Faculty of Science and Technology

Universiti Kebangsaan Malaysia, 43600, UKM Bangi, Selangor, Malaysia

 

T. Yamauchi

Graduate School of Agriculture, Kyoto University, 6068502 Kyoto, Japan

 

Received: 13 August 2009 / Accepted: 29 December 2009

 

ABSTRACT

 

Magnetic paper were prepared via the in situ synthesis method with ferrites in the presence of polyethylenimine (PEI). In this work, the thermomechanical pulp (TMP) fibers were used due to low percentage of collapse lumen and the large lumen size for optimum loading degree. Four cycles of the reaction were performed on the TMP fibers with pH values of 4-10. It was found that variation of pH value played an important role in the loading degree of pulp during synthesis process. The magnetic, morphological and structural properties of the magnetic paper obtained were reported. At the optimum pH of 6.0, saturation magnetization was found to be 3.08 emu/g, remainance magnetization was 0.11 emu/g and coercive force was 12.64 Oe. The optimum loading degree was found to be 23.25%.

 

Keywords: Fibers; magnetic filler; paper; thermomechanical pulp

 

ABSTRAK

 

Kertas bermagnet telah disediakan melalui kaedah sintesis in situ ferit dengan kehadiran polietilenemina (PEI). Dalam kajian ini, gentian pulpa termomekanikal (TMP) digunakan kerana peratus kerebahan lumen gentiannya adalah rendah dan ia mempunyai saiz lumen yang besar bagi darjah pemasukan yang optimum. Empat kitaran tindak balas telah dijalankan ke atas gentian TMP menggunakan nilai-nilai pH 4-10. Didapati variasi nilai pH larutan memainkan peranan penting pada darjah pemasukan pulpa semasa sintesis. Sifat magnet, morfologi dan struktur kertas bermagnet yang diperolehi dilaporkan. Pada pH optimum 6.0, pemagnetan tepu ialah 3.08 emu/g, pemagnetan baki ialah 0.11 emu/g dan daya paksa ialah 12.64 Oe. Darjah pemasukan yang optimum didapati sebanyak 23.25%.

 

Kata kunci: Kertas; pengisi magnetik; gentian pulpa termomekanikal

 

REFERENCES

 

Ainun Zuriyati. 2006. Penambahan poliakrilamida di dalam penyediaan kertas magnet lumen berpengisi. PhD thesis, Universiti Kebangsaan Malaysia

Akamatsu, I., Kobayashi,Y., Kamishima, H., Hassan, K., Mohd Yusof, M.N., Husin, M. & Hassan, A.H. 1987. Industrial utilization of oil palm by-products. II: thermomechanical pulping of empty fruit bunches. Cellul. Chem. Technol. 21: 191–197.

Chinga-Carrasco, G., Lenes, M., Johnsen, P.O. & Hult, E.L. 2009. Computer-assisted scanning electron microscopy of wood pulp fibres: Dimensions and spatial distributions in a polypropylene composite. Micron 40: 761-768.

Humaizah. 2006. Penyediaan kertas bermagnet dengan menggunakan magnetite (Fe3O4) dari tandan kosong kelapa sawit-PAM. MSc thesis Universiti Kebangsaan Malaysia.

IllŽs, E. & Tomb‡cz, E. 2006. The effect of humic acid adsorption on pH-dependent surface charging and aggregation of magnetite nanoparticles. Journal of Colloid and Interface Science 295: 115-123.

Marchessault, R.H, Rioux, P. & Ricard, S. 1992. Preparation and synthesis of magnetic fibers. US Patent No. 5143583.

Pulkkinen, I., Ala-Kaila, K. & Aittamaa, J. 2006. Characterization of wood fibers using fiber property distributions. Chemical Engineering and Processing 45: 546-554.

Ricard, S. & Marchessault, R.H. 1990. Preparation of in situ magnetically loaded cellulose fibers. Mat Res. Soc. Symp. Proc 197: 319-324.

Rioux, P., Ricard, S. & Marchessault, R. H. 1992. The preparation of magnetic papermaking fibres. Journal of Pulp and Paper Science 18: 39-43.

Wang, C., Ren, B., Tong, Z., Zeng, F., Liu, X., Wu, S. & Liu, P. 2005. Fluorescence observations on complex formation between linear and hyperbranched polyelectrolytes in dilute aqueous solutions. European Polymer Journal 41: 185-191.

Wanrosli, W.D., Zainuddin, Z., Law, K.N. & Asro, R. 2007. Pulp from oil palm fronds by chemical processes. Industrial Crops and Products 25: 89-94.

Zakaria, S., Ong, B. H., Ahmad, S. H., Abdullah, M. & Yamauchi, T. 2005. Preparation of lumen-loaded kenaf pulp with magnetite (Fe3O4). Materials Chemistry and Physics 89: 216-220.

Zhitomirsky, I. 2004. Electrochemical processing and characterization of nickel hydroxide-polyelectrolyte films. Materials Letters 58: 420-424.

 

*Corresponding author; email: rosefarahiyan@yahoo.com

 

 

previous