AC Susceptibility and Electrical Properties of PbS added Bi1.6Pb0.4Sr2CaCu2O8 Superconductor

(Kerentanan Arus Ulang Alik dan Sifat Elektrik Superkonduktor Bi1.6Pb0.4Sr2CaCu2O8 dengan Penambahan PbS)

 

M.J. MASNITA1,2, ROZIDAWATI AWANG2 & R. ABD-SHUKOR2*

 

1Fakulti Sains Gunaan, Universiti Teknologi MARA, 40450 Shah Alam, Selangor Darul Ehsan, Malaysia

 

2Department of Applied Physics, Universiti Kebangsaan Malaysia, 43600 UKM Bangi, Selangor Darul Ehsan, Malaysia

 

Received: 9 March 2021/Accepted: 22 April 2021

 

ABSTRACT

The Bi1.6Pb0.4Sr2CaCu2O8 (Bi-2212) phase is an interesting superconductor. Although it’s transition temperature is lower than Bi1.6Pb0.4Sr2Ca2Cu3O10 (Bi-2223), it has a better high field performance at low temperatures. This report is regarding the effects of lead sulfide on Bi1.6Pb0.4Sr2CaCu2O8 superconductor. Samples of Bi1.6Pb0.4Sr2CaCu2O8(PbS)x for x = 0.0 to 10.0 wt.% were prepared via the solid-state-reaction route. The Bi-2212 was the majority phase in all samples with x ≤ 1.0 wt.% showing more than 95%. Scanning electron micrographs showed increase in grain size as PbS content was increased. The x = 0 sample exhibited the highest T c-zero at 72 K and Tc-onset 83 K. The imaginary part of the AC susceptibility showed that the peak temperature, Tp increased from 59 K for x = 0 to 66 K for x = 0.6 wt.% sample. This research showed that PbS increased the flux pinning of Bi-2212 for x ≤ 1.0 wt.% although the transition temperature was suppressed.

 

Keywords: AC susceptibility; lead sulfide; microstructure; X-ray diffraction

 

ABSTRAK

Fasa Bi1.6Pb0.4Sr2CaCu2O8 (Bi-2212) adalah superkonduktor yang menarik. Walaupun suhu peralihannya lebih rendah daripada Bi1.6Pb0.4Sr2Ca2Cu3O10 (Bi-2223), ia mempunyai prestasi medan tinggi yang lebih baik pada suhu rendah. Penyelidikan ini adalah mengenai kesan plumbum sulfida terhadap superkonduktor Bi1.6Pb0.4Sr2CaCu2O8. Sampel Bi1.6Pb0.4Sr2CaCu2O8(PbS)x untuk x = 0.0 hingga 10.0 wt.% disediakan melalui tindak balas keadaan pepejal. Fasa Bi-2212 adalah majoriti dalam semua sampel dengan x ≤ 1.0 wt.% menunjukkan lebih daripada 95%. Mikrograf elektron imbasan menunjukkan peningkatan saiz butiran dengan peningkatan kandungan PbS. Sampel x = 0 menunjukkan T c-sifar tertinggi pada 72 K dan Tc-mula tertinggi pada 83 K. Bahagian khayal kerentanan arus ulang alik ” menunjukkan suhu puncak, Tp yang meningkat daripada 59 K untuk x = 0 hingga 66 K untuk sampel x = 0.6 %. Kajian ini menunjukkan bahawa PbS meningkatkan pengepinan fluks Bi-2212 untuk x ≤ 1.0 wt.% walaupun suhu genting menurun.

 

Kata kunci: Kerentanan arus ulang alik; mikrostruktur; pembelauan sinar-X; plumbum sulfida

 

REFERENCES

Aguiar, J.A., Lima, C.L.S., Yadava, Y.P., Tellez, D.L., Ferreira, J.M. & Montarroyos, E. 2000. EDX analysis, microstructureand magnetic properties of CuS doped Bi-2212 superconductors. Physica C: Superconductivity 341-348(Part 1): 593-596.

Aguiar, J.A., Ramos, A.S., Cabral, L.R., Barbosa, M.V., Awana, V.P.S., Ferreira, J.M., Pavão, A.C., Chavira, E. & Kurmaev, E.Z. 1996. Structural and superconducting properties of MS (M = Fe, Ni or Zn)-substituted YBa2Cu3O7-δ. Journal of Physics: Condensed Matter 8(49): 10545-10550.

Azhan, H., Hawa, J.S., Azura, C.M.N., Azman, K. & Syamsir, S.A. 2016. Structural and electrical properties of high and low Yb doped in Bi2223. Jurnal Teknologi 78(6-6): 7-12.

Brebrick, R.F. & Scanlon, W.W. 1954. Electrical properties and the solid-vapor equilibrium of lead sulfide. Physical Review 96(3): 598-602.

Darsono, N., Yoon, D-H. & Raju, K. 2016. Effects of the sintering conditions on the structural phase evolution and Tc of Bi1.6Pb0.4Sr2Ca2Cu3O7 prepared using the citrate sol-gel method. Journal of Superconductivity and Novel Magnetism 29(6): 1491-1497.

Dietderich, D.R., Ullmann, B., Freyhardt, H.C., Kase, J., Kumakura, H., Togano, K. & Maeda, H. 1990. Textured thick films of Bi2Sr2Ca1Cu2Ox. Japanese Journal of Applied Physics 29 (Part 2, No.7): L1100-L1103.

Dong, Y., Sun, A., Zhang, H., Zhang, M. & Xu, B. 2016. The effect of Sn substitution of Pb on microstructure and superconducting properties of Bi-Pb-Sr-Ca-Cu-O superconductor. Journal of Superconductivity and Novel Magnetism 29(11): 2765-2769.

Farah-Elia, N.A.R., Ilhamsyah, A.B.P. & Abd-Shukor, R. 2019. Ferrimagnetic Cr2S3 effects on (Bi1.6Pb0.4)Sr2CaCu2O6 superconductor. Journal of Materials Science: Materials in Electronics 30(13): 12031-12035.

Kaya, C., Özçelik, B., Özkurt, B., Sotelo, A. & Madre, M.A. 2012. Effect of Ce substitution on structural and superconducting properties of Bi-2212 system. Journal of Material Science: Materials in Electronics 24(5): 1580-1586.

Loudhaief, N., Salem, M.B., Labiadh, H. & Zouaoui, M. 2020. Electrical properties and fluctuation induced conductivity studies of Bi-Based superconductors added by CuS nanoparticles synthesized through the aqueous route. Materials Chemistry and Physics 242: 122464.

Marken, K.R., Dai, W., Cowey, L., Ting, S. & Hong, S. 1997. Progress in BSCCO-2212/silver composite tape conductors. In IEEE Transaction on Applied Superconductivity. IEEE. 7(2): 2211-2214.

Marken, K.R., Miao, H., Meinesz, M., Czabaj, B. & Hong, S. 2003. BSCCO-2212 Conductor development at oxford superconducting technology. In IEEE Transaction on Applied Superconductivity 13(2): 3335-3338.

Muhammad-Aizat, K. & Abd-Shukor, R. 2018. Electrical properties and AC-susceptibility of CdTe added Tl2Ba2CaCu2O8-δ superconductor. Sains Malaysiana 47(7): 1579-1583.

Pearce, C.I., Pattrick, R.A. & Vaughan, D.J. 2006. Electrical and magnetic properties of sulfides. Reviews in Mineralogy and Geochemistry 61(1): 127-180.

Sahoo, M. & Behera, D. 2013. SCOPF analysis of YBa2Cu3O7-δ + Cr2O3 superconductor composite. Journal of Physics and Chemistry of Solids 74(7): 950-956.

Shimoyama, J.I., Kadowaki, K., Kitaguchi, H., Kumakura, H., Togano, K., Maeda, H. & Nomura, K. 1993. Processing and fabrication of Bi2Sr2CaCu2Oγ/Ag tapes and small scale coils. Applied Superconductivity 1(1-2):  43-51.

Tenbrink, J., Wilhelm, M., Heine, K. & Krauth, H. 1993. Development of technical high-tc superconducting wires and tapes. In IEEE Transaction on Applied Superconductivity 3(1): 1123-1126.

Tyagi, A.K. & Sharma, T.P. 1994. Metallurgical reactions and enhanced magnetic field shielding in YBCO-PbS superconductor. Materials Letters 18(5-6): 341-348.

Yahya, N.A. & Abd-Shukor, R. 2014. Effects of nano-sized PbO on the transport critical current density of (Bi1.6Pb0.4Sr2Ca2Cu3O10)/Ag tapes. Ceramics International 40(4): 5197-5200.

Yavuz, Ş., Bilgili, Ö. & Kocabaş, K. 2016. Effect of superconducting parameter of SnO2 nanoparticles addition on (Bi, Pb)-2223 phase. Journal of Materials Science: Materials in Electronics 27(5): 4526-4533.

Yusrianto, E., Jannah, A.N. & Abd-Shukor, R. 2021. Phase formation and critical temperature of (Tl0.5Pb0.5)Sr2Ca(Cu2-xCrx)O7-δ (x = 0 - 0.100) superconductor. Sains Malaysiana 50(6): 1775-1786.

Zhou, X.X., Xue, F., Gou, X. & Shen, T.M. 2019. Statistical study of the void structure of Bi2212 multifilamentary superconductors wires and its effect on the critical current density. Engineering Computations 36(8): 2714-2725.

 

*Corresponding author; email: ras@ukm.edu.my

     

 

 

previous